![]() | ERCCoCr-E焊絲ERCCoCr-E焊絲是用鉬強化的低碳鈷鉻合金,在室溫下硬度較低,但冷作后硬度有所提高。堆焊層具有良好的耐高溫腐蝕,耐沖擊能和良好的高溫強度 . |
| Oxford Alloy?#21M | |
| SPECIFICATIONS | CLASSIFICATIONS |
| AWS 5.21 | AWS ERCCoCr-E |
| ASME SFA 5.21 | UNS W73041 |
Oxford Alloy #21M is an alloy-cored wire for GMAW applications with excellent high temperature strength making it suitable for use on hot dies. The deposits of this alloy are inherently resistant to galling, cavitation erosion, and corrosion. Abrasion resistance of the Oxford Alloy #21M is lower than other wires but its impact strength at high temperatures; anti-galling properties and corrosion resis-tance are outstanding. Oxford Alloy #21M should be welded with direct current reverse polarity requiring proper preheat, interpass temperatures and controlled cooling to minimize or produce a crack free deposit. Some applications that the Oxford Alloy #21M is used for are fluid valve seats, tube mill piercing plugs, hot shears, erosion shields, and forging dies.
| AWS Chemical Composition | ||||||
| C | Mn | Si | Cr | Mo | Fe | Ni |
| 0.15-0.40 | 2.0max | 1.5max | 25-30 | 4.5-7.0 | 5.0max | 1.5-4.0 |
| Co | W | OET | ||||
| Bal | 0.50max | 1.0max | ||||
| TYPICAL MECHANICAL PROPERTIES | |
| Rockwell Hardness: | 20-35 HRC |
Note: The typical hardness values listed above are for multilayer welds. Hardness values for single deposits will be lower because of dilution from the base metal.